Textbook Question
Chapter 7.10, Problem 26AAP
A Ti-6Al-4V alloy plate contains an internal through crack of 1.90 mm. What is the highest stress (MPa) that this material can withstand without catastrophic failure? What is the highest stress if the internal crack is 0.95 mm (half of that in part a)? Assume
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
Compute the minimum critical surface crack (edge crack) length if the fatigue life must be a minimum of 5.0 x 106 cycles. Assume the initial maximum edge surface crack length of 1.80 mm and a maximum tensile stress of
160 MPa and minimum stress of 0 MPa. Assume m = 1.8 and A= 7.5 x 1013 in MPa and meter units, Assume Y= 1.25.
O a. 4.26 mm
O b. 5.38 mm
OC. 2.36 mm
O d.0.125 m
3- Using the equation Kic= of Vna, plot the fracture stress (MPa) for aluminium alloy 7075-
T651 versus surface crack size a (mm) for a values from 0.2 mm to 2.0 mm. What is the
minimum size surface crack that will cause catastrophic failure? KỊc=24.2 Mpavm
A specimen of a steel alloy with a plane strain fracture toughness of 22.1 MPavm. The largest surface crack is 0.6 mm long? Assume that the parameter Y has a value of 0.5. What is
the critical stress in MPa. Write your answer with 2 decimal places.
Answer:
0
dºvo vo (0)
00
00,
GM
Chapter 7 Solutions
Foundations of Materials Science and Engineering
Ch. 7.10 - What are the characteristics of the surface of a...Ch. 7.10 - Prob. 2KCPCh. 7.10 - Prob. 3KCPCh. 7.10 - Prob. 4KCPCh. 7.10 - Prob. 5KCPCh. 7.10 - Prob. 6KCPCh. 7.10 - Prob. 7KCPCh. 7.10 - Prob. 8KCPCh. 7.10 - Prob. 9KCPCh. 7.10 - How does the carbon content of a plain-carbon...
Ch. 7.10 - Describe a metal fatigue failure.Ch. 7.10 - What two distinct types of surface areas are...Ch. 7.10 - Prob. 13KCPCh. 7.10 - Prob. 14KCPCh. 7.10 - Prob. 15KCPCh. 7.10 - Describe the four basic structural changes that...Ch. 7.10 - Describe the four major factors that affect the...Ch. 7.10 - Prob. 18KCPCh. 7.10 - Prob. 19KCPCh. 7.10 - Prob. 20KCPCh. 7.10 - Prob. 21KCPCh. 7.10 - Determine the critical crack length for a through...Ch. 7.10 - Determine the critical crack length for a through...Ch. 7.10 - The critical stress intensity (KIC) for a material...Ch. 7.10 - What is the largest size (in mm) of internal...Ch. 7.10 - A Ti-6Al-4V alloy plate contains an internal...Ch. 7.10 - Using the equation KIC=fa, plot the fracture...Ch. 7.10 - (a) Determine the critical crack length (mm) for a...Ch. 7.10 - A fatigue test is made with a maximum stress of 25...Ch. 7.10 - A fatigue test is made with a mean stress of...Ch. 7.10 - A large, flat plate is subjected to...Ch. 7.10 - Prob. 32AAPCh. 7.10 - Refer to Problem 7.31: Compute the final critical...Ch. 7.10 - Prob. 34AAPCh. 7.10 - Prob. 35AAPCh. 7.10 - Equiaxed MAR-M 247 alloy (Fig. 7.31) is used to...Ch. 7.10 - Prob. 37AAPCh. 7.10 - If DS CM 247 LC alloy (middle graph of Fig. 7.31)...Ch. 7.10 - Prob. 39AAPCh. 7.10 - Prob. 40AAPCh. 7.10 - Prob. 41SEPCh. 7.10 - Prob. 42SEPCh. 7.10 - A Charpy V-notch specimen is tested by the...Ch. 7.10 - Prob. 44SEPCh. 7.10 - Prob. 45SEPCh. 7.10 - Prob. 46SEPCh. 7.10 - Prob. 47SEPCh. 7.10 - Prob. 48SEPCh. 7.10 - Prob. 49SEPCh. 7.10 - Prob. 50SEPCh. 7.10 - While driving your car, a small pebble hits your...Ch. 7.10 - Prob. 52SEPCh. 7.10 - Prob. 53SEPCh. 7.10 - Prob. 54SEPCh. 7.10 - Prob. 56SEPCh. 7.10 - Prob. 57SEPCh. 7.10 - Prob. 58SEPCh. 7.10 - Prob. 59SEPCh. 7.10 - The components in Figure P7.60 are high-strength...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
What is the weight in newtons of an object that has a mass of (a) 8 kg, (b) 0.04 kg, (c) 760 Mg?
Statics and Mechanics of Materials (5th Edition)
Compute the hydraulic radius for a circular drain pipe running half full if its inside diameter is 300 mm.
Applied Fluid Mechanics (7th Edition)
A biological fluid moves at a flow rate of m=0.02kg/s through a coiled, thin-walled, 5-mm-diameter tube submerg...
Fundamentals of Heat and Mass Transfer
Determine the length of the cantilevered beam so that the maximum bending stress in the beam is equivalent to t...
Mechanics of Materials (10th Edition)
A windowmounted air conditioner removes 3.5kJ from the inside of a home using 1.75 kJ work input. How much ener...
EBK FUNDAMENTALS OF THERMODYNAMICS, ENH
Steady state conduction rate to the warm compressor to the net power produces theoretically by thermodynamic ba...
Introduction to Heat Transfer
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- A metallic tube has an outer diameter of 500 mm and a wall thickness of 30 mm (Figure 4). The working internal pressure of the tube is 15 MPa and the fracture toughness of the material (K₁c) ranges from 40 MN/m³/2 to 50 MN/m³/2. Select a value for Kic and determine the size of the largest flaw the tube can contain. Assume that for this geometry K σφπα. = 30 mm! 500 mm Figure surface flaws 4 (not to scale)arrow_forwardA cast iron cylinder has outside and inside diameter 200mm and 125mmrespectively. If the ultimate strength of cast iron is 150MPa calculate according to each of the following theories of failure the internal pressure that will cause fracture.(a) Maximum principal stress theory. (b) Maximum principal strain theory. (c) Maximum strain energy theory. Assume no longitudinal stress in the cylinder. Which of the results obtained you consider should be applied to this case. Take:µ = 0.25, σU = 150MPa. Ans: (a) 65.73MPa. (b) 59.24MPa, (c) 55.33MPa.arrow_forwardA tie rod made of quenched and tempered 4340 steel is used as a critical linkage in an industrial apparatus. The rod is subjected to an alternating cyclic tensile/compressive stress from 550 MPa to -550 MPa. An inspection of the rod revealed a 3.5 mm deep edge crack on the surface of the rod. Please answer the following question for the rod given the properties in the table and curve below and fracture toughness of 55 MPa√m. (NOTE: Y=1.12 for edge crack and use “a” not “2a” for the length of the crack) 1. Given the S-N curve for 4340 steel, is there an endurance limit? If so, what is the stress value for the endurance limit? 2. If there were no cracks and the stress on the rod still alternated from 550 MPa to -550 MPa with mean stress of zero, what would be the cycles to failure?arrow_forward
- A tie rod made of quenched and tempered 4340 steel is used as a critical linkage in an industrial apparatus. The rod is subjected to an alternating cyclic tensile/compressive stress from 550 MPa to -550 MPa. An inspection of the rod revealed a 3.5 mm deep edge crack on the surface of the rod. Please answer the following question for the rod given the properties in the table and curve below and fracture toughness of 55 MPa√m. (NOTE: Y=1.12 for edge crack and use “a” not “2a” for the length of the crack) 1. At the given crack size and tensile loading would the rod undergo instantaneous fast fracture, assuming plane strain conditions? Show calculations to back up your conclusions.arrow_forwardA tie rod made of quenched and tempered 4340 steel is used as a critical linkage in an industrial apparatus. The rod is subjected to an alternating cyclic tensile/compressive stress from 550 MPa to -550 MPa. An inspection of the rod revealed a 3.5 mm deep edge crack on the surface of the rod. Please answer the following question for the rod given the properties in the table and curve below and fracture toughness of 55 MPa√m. (NOTE: Y=1.12 for edge crack and use “a” not “2a” for the length of the crack) 1. What is the minimum crack size that would cause instantaneous fast fracture at the current maximum axial tensile loading, assuming plane strain conditions apply? If the resolution limit of the flaw detection apparatus were 1.5 mm, would this flaw be subject to detection? Show calculations to back up your conclusions.arrow_forwardQuestion 2 A machine component is made of Aluminium alloy having an ultimate tensile stress Ou = 350MPa, a fracture toughness Kic= 40 MPa√m and a geometry factor Y=1.12. The component is subject to cyclic tensile stress of 200 MPa and cyclic compressive stress of 70 MPa. Before the operation, using an ultrasonic non-destructive testing technique, it was found that there is an edge crack of length 2mm. The crack growth C(AK)m, where is in m/cycle, AK ΔσΥ νπα , C ~ 2.2×10-12 da rate is given by da dN dN and m=3.2. Find the critical crack length. = =arrow_forward
- (ii) The turbine blade root is found to contain a surface fatigue crack of 3.3 mm during a routine maintenance inspection. The major stop-start load cycle is experienced twice per day with a minimum stress of 34 MPa and a maximum stress of 195 MPa. The turbine blade has a KIC of 75 MPa√m. Fatigue crack growth rate data for this alloy is given by: the Paris law constant, A = 4.5 x 10-11 and the Paris law exponent, m = 3.8. How many more stop-starts would you recommend be used? Explain your reasoning. You can assume the shape factor Q = 1.2, K is in MPaNm and a (crack length) is in marrow_forwardQuestion 1 The S-N diagram for a titanium alloy is shown in the figure. Calculate the fraction of life consumed by the following sequence of loadings: 15,000 cycles at 80 MPa 120,000 cycles at 60 MPa 3,500,000 cycles at 50 MPa Maximum stress (ksi) 160 140 120 100 80 60 40 20 I 10³ 104 105 Cycles to failure 100 107arrow_forward(a) An AISI 4340 steel plate has a width W of 30 cm and has a central crack 2a of 3 mm. The plate is under a uniform stress σ. This steel has a KIc value of 50 MPa m1/2. Find the maximum stress for this crack length. (b) If the operating stress is 1,500 MPa, compute the maximum crack size that the steel may have without failurearrow_forward
- A cylindrical steel pressure vessel D-575 mm in diameter with a wall thickness of 5 mm is subjected to an internal pressure of 3 MN/m². Calculatea- the tangential and longitudinal stresses in the steel.b- To what value may the internal pressure be increased if the stress in the steel is limited to 80 MN/ m²?c-If the internal pressure were increased until the vessel burst, sketch the type of fracture that would occurarrow_forwardA component made of 7075-T6 aluminum alloy has an edge crack of 1.4 mm in length. Plane strain fracture toughness of this alloy is given as 27 MPavm. Geometrical factor of the crack is given as 1.2. (a) If this alloy is subjected to uniaxial tensile stress of 380 MPa, determine whether sudden brittle fracture occurs or not. (b) Calculate the maximum allowable crack size for this component in order not to be failed in brittle manner under a stress of 1000 MPa (Density of steel 7.85 g/cm³, 9.80665 N = 1 kg). Modulus of elastisity, GPa Ultimate tensile Yield strength, Alloy strength, MPa MPa 2014 Al alloy Bronze (92Cu-8Sn) High carbon steel Pure Titanium 97 186 380 72 110 152 380 615 215 240 330 107arrow_forward1. An element is to be subjected to a spectrum of completely reverse stress. It will be cycled at 460 MPa for 29000 cycles. Then the stress will be changed to 440 MPa for 65000 cycles. Finally, the stress will be changed to 315 MPa. How many cycles of operation can be expected at this stress level? Known that the material has endurance limit of 320 MPa, material constant m = 10,9 and critical number of cycles No = 7x10". Ans. Infinityarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Understanding Failure Theories (Tresca, von Mises etc...); Author: The Efficient Engineer;https://www.youtube.com/watch?v=xkbQnBAOFEg;License: Standard youtube license