The figure below shows the stress strain diagram of a cortical bone, with initiallyrectangular cross section of 15 x 20 mm2, and length of 10 cm. using this figuredetermine:a) The elastic modulusb) The yield strengthc) The ultimate strength.d) The corresponding ultimate true stress, if you know that the instantaneous crosssection was at this point was 12 x 17 mm?.e) The deformed length corresponding to the ultimate strength.f) The poison's ratio corresponding to the ultimate strength for the following twocases:a. Use the 15 mm as the undeformed specimen width.b. Use the 20 mm as the undeformed specimen width 30300250Eperimental Murement200150100500.020.040.060.080.10.120.140.160.18StreinStress (MPa)多

As per our company policy we are asked to solve 3 sub-parts of a question.. Please post rest parts…

The figure below shows the stress strain diagram of a cortical bone, with initially rectangular cross section of 15 x 20 mm2, and length of 10 cm. using this figure determine: a) The elastic modulus b) The yield strength c) The ultimate strength.

The figure below shows the stress strain diagram of a cortical bone, with initially rectangular cross section of 15 x 20 mm2, and length of 10 cm. using this figure determine: a) The elastic modulus b) The yield strength c) The ultimate strength.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in.in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lblb - in.in. per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.
Table B2: Stress-strain data for uniaxial compression test on Sample Normal stress Uniaxial strain (%) Lateral strain (%) (MPa) 0.0 0.0000 0.0000 5.0 0.0319 -0.0150 10.0 0.0720 -0.0275 15.0 0.1025 -0.0425 20.0 0.1450 -0.0600 25.0 0.1755 -0.0725 30.0 0.2150 -0.0875 35.0 0.2455 -0.1025 41.0 0.2815 -0.1125 46.0 0.3125 -0.1209 52.0 0.3515 -0.1285 58.0 0.4000 -0.1325 (f) Based on the plotted curve, calculate the average/tangent Young's modulus and Poisson's ratio for this sample, at 50 % UCS?
A 11 in. inner diameter, 0.35 " wall thickness pipe is under a pressure of 2.5 ksi where strain gages installed along axial and circumferential directions register strains of 180 and 900 micro-strains (x10^-6), respectively. A) What is the Poisson's Ratio of this material and it's Elastic Modulus? B) In a uniaxial test, the pipe's material is observed to yield at a longitudinal strain of 0.1 in/in. Assuming a factor of safety of 2, the pipe can withstand impact energy of _______ lb - in per foot without suffering permanent deformation. C) If the pipe is depressurized and then subjected to a torque of 50 lblb - ft.ft., it will experience a shear strain of ________ rad.
Ql- mm ,length 40 mm. The final diameter 18 mm and length 45 mm. Draw the force-extension diagram and determine the following : a) Ultimate tensile strength, c) Modulus of elasticity, d) Percent elongation and e) Percent reduction in area. The following data collected from tensile test of a metal bar diameter 20 b) The fracture strength, Force - kN 75 90 | 105 120 131 125 110 25 50 4.7 Extension-mm 0.02 0.04 0.06 0.20 - 0.60 1.60 3.00 4.0 Fracture
A Copper specimen of circular cross-section is subjected to a tensile test. The data obtainedare:Length of Specimen = 329 mm;Diameter of Specimen = 39 mm;Load at Yield Point = 130 kN;Maximum Load = 219 kN;Load at fracture = 118kNDetermine the following:1) Find initial area of the test specimen2) Yield Stress3) Ultimate Stress4) Fracture stress5) Find the strain for 0.058mm elongation.6) Mark Yield stress, Ultimate stress and Fracture stress on a Stress-Strain diagram.
a . Sketch stress strain curve if the result shown in table represent the force and extension happened in steel, and show Mechanical properties that we get from tensile test on curve? (10p)Note : Lo=80 mm , Do=10 mm , use excel to plot the curve ExtensionLoad(mm) (N)0 0.900.83 4694.341.67 4831.412.50 4781.083.33 4918.834.17 4926.585.00 5257.075.83 5437.016.66 5575.888.33 5775.189.16 5847.5210.83 5965.4111.67 6010.5312.50 6042.5713.33 6072.2614.16 6092.9315.00 6113.2416.67 6140.3617.50 6146.3718.33 6148.1419.16 6149.1725.00 5940.2125.83 5675.3326.67 4725.52b. What is meant by modulus of rigidity? if it increases what does happen to material? (2p)
5. Please calculate the strain and stress in the following two prompts a. A 1 cm long section of tendon stretches to 1.011 cm when it is subjected to a tensile force of 40,000 N. What is the strain in this segment of tendon? @? 17 b. The section of the patellar ligament in the previous question is 0.02 m² in the cross section. What is the stress in this section of ligament as a result of 50,000 N tensile force? E = Δι 19 0 = A 1.011 cm 50000 0,02 Scoco 40000 1.25 = T % 2500000 strain N/m² on trito flox your wrist, you may notice that your
The figure below is a stress strain curve for an alloy of aluminum at various temperatures. a) What is the yield stress at room temperature? b) Assume a rod made of this material is 20 cm long and at room temperature. If the rod were put in tension, how long would it be when it breaks? c) If the rod has cross-sectional area 1 cm?, what force is required to break it (in tension)? Longitudinal RT 250F 350F 30 500F 0.002 0.004 0.006 0008 QO10 O012 Strain, in/in. A-93 Stress, ksi
A mild steel specimen of Young's Modulus 205 GPa is subjected to a tensile test in a laboratory. The following data are obtained. a) Initial length of the Specimen = 362 mm; b) Initial diameter of Specimen = 19 mm; c) Yield Stress = 123 N/mm2; d) Ultimate Stress = 225 N/mm2; e) Fracture Stress = 190 N/mm2; g) % of Elongation = 56 %; h) % of Reduction in Area = 29 %. i) The elongation of the specimen at load 83 kN (in mm) ii) Load at yielding (in N) iii) Maximum load (in N) iv) Final Length (in mm) v) Final Diameter (in mm)
4. We want to draw a 7.5 mm diameter copper wire having a yield strength of 140 MN.m²² into a 6 mm diameter wire. Will the drawn wire break during the drawing process? Strength (MN.m-2) 600 500 400 300 200 100 0 0 Tensile strength 20 Yield strength % Elongation 60 40 Percent cold work 80 100 90 80 70 60 50 40 30 20 10 100 % Elongation
1. Concept questions in forms of multiple choices, filling blanks, and/or computations. a) According to Eq. (3-15) on p.109 of the textbook, the roots from: o³ – 40? – 40 - 5 = 0 represent the three principal stresses of a 3D stress state. True False b) The transverse shear should be not significant in very long beam. True False c) A fixed-end beam is easier to buckle than a fixed-free end beam to buckle. True , False d) Distortion energy theory is mainly for the torsion failure analysis. True False e) The fracture toughness obtained from a thin sheet specimen should be higher than that from a thick block specimen assuming that the same material is tested. True False
n=0,10 F Strain Stress n=019 9) Give an example of: i) a truly elastic material:..... ...ii) a material which is not viscoelastic:.... 10) If you require fatigue resistance for an application, among all manufacturing methods (machining, forging rolling casting deen drawing hich wath