Q1-. A 1m long metal is stretched so that it increases in length incrementally in four passes by an amount of 0.025cm in each pass. Determine: (i) the four incremental true strains; (ii) the total true strain; (iii) the fours incremental engineering strains; (iv) the total engineering strain; (v) From your solutions, show that for engineering strains, the strain for each step cannot simply be added to obtain the total strain; and Ans:0.0951 0.1 6.

Q1-. A 1m long metal is stretched so that it increases in length incrementally in four passes by an amount of 0.025cm in each pass. Determine: (i) the four incremental true strains; (ii) the total true strain; (iii) the fours incremental engineering strains; (iv) the total engineering strain; (v) From your solutions, show that for engineering strains, the strain for each step cannot simply be added to obtain the total strain; and Ans:0.0951 0.1 6.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

How can the principal normal strains and maximum in-plane shear strain be determined?
2) The strength coefficient and strain-hardening exponent of a certain test metal are 750 MPa and 0.25, respectively. A cylindrical specimen of the metal with starting diameter = 75 mm is stretched. If the average flow stress on the part is 450 MPa determine the final diameter of the specimen.
2. The flow curve parameters for a certain stainless steel are strength coefficient = 1100 MPa and strain-hardening exponent = 0.35. A cylindrical specimen of starting cross-sectional area = 1000 mm? and height = 75 mm is compressed to a height of 58 mm. Determine the force required to achieve this compression, assuming that the cross section increases uniformly.
In True stress-true-strain curve in tension of solid metal cylinder 45 mm high and 8 mm in diameter, two pairs of values of stress and strain were given for the specimen metal after it had yielded (1) true stress = 217 MPa, and true strain = 0.35; and (2) true stress = 259 MPa, and true strain = 0.68. Based on these data points, determine the following: a) The average flow stress that the metal experiences if it is subjected to a stress that is equal to its strength coefficient K. b) The work done that the metal experiences if it is subjected to elongation in height of 45% c) If during the deformation the relative speed = 20 mm/s, determine the strain rate at h = 50 mm and h = 70 mm.
A material has a linear elastic perfectly plastic stress-strain. A cylindrical specimen of that material having an initial length of 35 mm and a tadius of 7 mm is pulled until it elongates 0.8mm. a. Calculate the stain and the corresponding stress at that elongation value. b. Afterward, the specimen is released to zero stress level, how does the final length of the specimen compare with its original length? How much plastic deformation remains if it exists?
. From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please answer the following questions (1) Estimate the modulus of elasticity, (2) Calculate the change in length of a specimen with original length of 100mm that is subjected to a tensile stress of 300MPa. (Hint: Using the Hooke's law to get the strain.) 600 500 400 - 300 - 200 - 100 - 2 4 6. 8 10 12 14 16 Strain Strength (MPa)
From the tensile stress-strain behavior for the brass specimen shown in Figure 6.12, determine the following: (a) The modulus of elasticity (b) The yield strength at a strain offset of 0.002 (c) The maximum load that can be sustained by a cylindrical specimen hav- ing an original diameter of 12.8 mm (0.505 in.) (d) The change in length of a specimen originally 250 mm (10 in.) long that is subjected to a tensile stress of 345 MPa (50,000 psi)
True stress-strain Engineering stress-strain strain Calculate the engineering ultimate tensile strength of a material whose strength coefficient is 535 MPa and of a tensile-test specimen that necks at a true strain of 0.55. 200 MPa O 267 MPa O 244 MPa O 222 MPa stress
Q.1. In a creep test, a material with E = 600 MPa is initially loaded with a stress o, = 297 MPa. 1.5 hr after the initial loading, the strain in the material is measured to be 0.12, and after another hour, it is found to be 0.1832. What will be the strain in the material 3 hours after the initial %3D loading? How much time did it take for the strain to reach a value of 0.001?
A 3-mm-long gold alloy wire intended to electricallybond a computer chip to its package has an initial diameter of30 μm. During testing, it is pulled axially with a load of 15grams-force. If the wire diameter decreases uniformly to29 μm, compute the following:a. The final length of the wire.b. The true stress and true strain at this load.c. The engineering stress and strain at this load.
Question 4 You do a series of tensile tests on plates of a magnesium alloy that have been subjected to prior cold rolling to true plastic strains of 0.1, 0.2 and 0.3. The resulting true stress-true strain curves are shown below (including a zoomed in version expanding on the small strain region). It is reasonable to approximate the the 0.2% offset yield strength of the magnesium as ✓ MPa for 0.1 plastic strain, ✓ MPa for 0.2 and ✓ MPa for 0.3. Assuming the yield strength is proportional to the square root of the prior true plastic strain results in a hardening coefficient of approximately k= ✓ MPa. Hence, we can predict that we need a prior plastic strain of approximately ✓to obtain a hgth of 120 MPa True Stress (MPa) 250 200 100 85 95 50 105 115 125 135 145 300 350 0.12 0.14 150 0.16 0.18 155 165 175 200 250 0.1 True Stress (MPa) Ep = 0.1 Zoomed version of left plot
For some metal alloy, a true stress 345 MPa (50040 psi) produces a plastic true strain of 0.02. How much will a specimen of this material elongate when a true stress of 418 MPa (60630 psi) is applied if the original length is 500 mm (19.69in) ? Assume a value of 0.22 for the strain- hardening exponent, n