Drawing: A round rod of annealed 302 stainless steel (K = 1300 MPa and n = 0.3) is being drawn from a diameter of 15 mm to a diameter of 12 mm at a speed 0.25 m/s, using a semidie angle of 8°. a. Calculate the percentage reduction, the applied force due to ideal deformation, friction, and inhomogeneous deformation. Assume coefficient of friction of 0.1. b. Calculate the required power, process efficiency, and the die pressure at the exit.

Drawing: A round rod of annealed 302 stainless steel (K = 1300 MPa and n = 0.3) is being drawn from a diameter of 15 mm to a diameter of 12 mm at a speed 0.25 m/s, using a semidie angle of 8°. a. Calculate the percentage reduction, the applied force due to ideal deformation, friction, and inhomogeneous deformation. Assume coefficient of friction of 0.1. b. Calculate the required power, process efficiency, and the die pressure at the exit.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Please answer the mechanical question with a complete solution as soon as possible. Please include the shear and moment diagrams Thank you!
Assume you are bending a 3/16” thick rolled plate of Al 6061-T6 at a 90-degree angle. The initial bend radius (after the part is bent in the press brake) is 0.35”. Look up material properties on the Internet a) What is the final bend radius after the part has “relaxed”?b) Is it within the 2-4% rule of thumb?Show your work, and write down any values you choose to reference/use.
7. A strip of annealed low-carbon steel (K = 528 MPa, n = 0.25) is rolled from its initial dimensions (210 mm wide and 13 mm thick) to a thickness of 7 mm. The rollers have a radius of 250 mm, the roller rotates at 200 rpm, and u = 0.1. Compare this high frictional force and power with the low frictional (u = 0) forces and power. a. Estimate the roll force and power required for this process.
A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that the thickness is reduced, the plate is widened by 4%. The elastic limit of the steel plate is 174MPa and its resistance is 290MPa. The input speed of the plate is 15m/min. The radius of the cylinder is 52.8mm and the rotation speed is 49 revolutions per minute. Determine: a) The minimum coefficient of friction that will make this rolling operation possible. b) The output speed of the plate c) Slide forward
Ex: Wire is drawn through a draw die with entrance angle 15°. Starting diameter is 2.5 mm and final diameter 2.0 mm. The coefficient of friction at the work-die interface 0.07. The metal has a strength coefficient K=205 MPa and a strain- hardening exponent n = 0.20. Determine the draw stress and draw force in this operation.
In a single pass rolling bearing process using 510mm diameter steel rollers a strip of width 110mm and thickness 6mm undergoes 20%reduction of thickness. Find the angle of bite
Use method of consistent deformations. Give me right solution. Urgent
Two high rolling mill setup has been used to reduce the thickness of a plate from 40 mm at the maximum draft per pass to become 34 mm after the last pass. The width of the rolled material is 560 mm and the roll diameter is 560 mm. The material has a strength coefficient of 260 MPa and a strain hardening exponent of 0.18. The coefficient of friction during the process was 0.085. Determine the following: 1- Number of passes required to perform the reduction process = 2- Strain of the last pass = 3- Average flow stress of the last pass = MPa 4- The rolling force to roll the last pass =
Please give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100 in long. It is reduced in one pass in a two-high rolling mill to a thickness = 3.5 in. The roll rotates at a speed = 12 rev/min and has a radius = 20 in. The aluminum has a strength coefficient = 25,000 lb/in2 and a strain hardening exponent = 0.20. Determine the (a) roll force, (b) roll torque, and (c) power required to accomplish this operation, d) Estimate the GHG emission in an hour for the rolling operation.
(3) A machine part of uniform thickness t = b/2.5 is shaped as shown and machined all over from AISI C1020, as 2b rolled. The design is for indefinite life for a load repeated from 1,750 lb to 3,500 lb. Let d = b. (a) For a design factor of 1.8 (Soderberg), what should be the dimensions of the part? (b)What is the maximum tensile stress in the part as designed? (4) The same as Problem No. 3, except that cycles of loading should not exceed 10.
A solid piece of steel 60 mm in diameter and 80 mm height is reduced in height by 50 percent with the help of open die forging. The work material characteristics are represented by k = 350MPA and n = 0.16. If coefficient of friction is 0.1, find the maximum forging force.
A rectangufar workpiece has the following original dimensions: 2a = 120 mm, h = 40 mm and width = 25 mm (see Fig. 6.5). The metal has a strength coefficient of 530 MPa and a strain hardening exponent of 0.26. It is being forged in-plane strain with u = 0.25. Calculate the force required at a reduction of 25%. Use the average- Question 2 Not yet answered Marked out of 5 pressure formula. P Flag question