A mild steel bar of 2cm is subject to tensile test. The bar yields under a load of 80kN. It reaches a maximum load of 150kN and breaks finally at a load of 70kN. Estimate the a) Average tensile stress at yield point b) ultimate tensile stress c) average stress at the breaking point if the diameter of the fractured neck is 1cm

A mild steel bar of 2cm is subject to tensile test. The bar yields under a load of 80kN. It reaches a maximum load of 150kN and breaks finally at a load of 70kN. Estimate the a) Average tensile stress at yield point b) ultimate tensile stress c) average stress at the breaking point if the diameter of the fractured neck is 1cm

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. a. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length. Step-by-step solution: Step 1 of 4 Given that: Width of the specimen, b = 1 in Thickness of the specimen, t = 0.25 in Yield load on the specimen, Py = 12.5 kips Fracture load on the specimen, Pf = 17.5 kips Gauge length, L = 2 in Percentage of yield stress = 60%
3. A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips. а. Determine the tensile stresses at yield and at fracture. b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length
A steel specimen is tested in tension. The specimen is 1.0 in. wide by 0.25 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 12.5 kips and fractured at 17.5 kips.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much increase in length would occur at 60% of the yield stress in a 2-in. gauge length.
= Syc = 100 kpsi and a true strain at fracture = 0.55. Estimate the factor of safety for the following principal stress states: A hot-rolled steel has a yield strength of Syf of ɛf = | (b) ox = 60 kpsi, ơy |(c) ơx |(d) ox = -40 kpsi, ơy |(a) 0x = 70 kpsi, ơy = 70 kpsi, txy 40 kpsi, txy 40 kpsi, txy = = -60 kpsi, Txy = 0 kpsi -15 kpsi 45 kpsi 0 kpsi, ơy = %3D 15 kpsi | (e) 01 = 30 kpsi, o2 = 30 kpsi, 03 = 30 kpsi
Problem 4: A tensile test is carried out on a bar of a mild steel of diameter 2 cm. the bar yields under a load of 150 kN and breaks finally at a load of 70 kN. Estimate; 1-the tensile stress at the yield point 2-the ultimate tensile stress 3-the average stress at the breaking point, if the diameter of the fractured neck is 1 сm.
A steel specimen is tested in tension. The specimen is 25 mm wide by 5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 55 kN and fractured at 78 kN.a. Determine the tensile stresses at yield and at fracture.b. Estimate how much elongation would occur at 60% of the yield stress in a 50-mm gauge length.
7) A specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation. (iv) Percentage reduction in area. (v) Ultimate tensile stress.
A steel specimen is tested in tension. The specimen is 1 in. wide by 0.5 in. thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 36 kips and fractured at 48 kips.a. Determine the tensile stress at yield and at fracture.b. If the original gauge length was 4 in., estimate the gauge length when the specimen is stressed to 1/2 the yield stress.
2. A specimen of steel 25mm diameter witha guage langth of 200 mm is tested to destruction. It has an extension of 0.16mm under a load of 80 kn and the load at elastic limit is 160 kN. The maximum load is 180 kN. The total extension at fracture is 56 mm and diameter at neck is 18 mm. Find a. The stress at elastic limit b. Youngs's Modulus c. Percentage elongation d. Percentage reduction in area e. Ultimate tensile stress
1. A specimen of steel 20 mm diameter with a gauge length of 200 n.m is tested io destruction. It' has an extension of 0.25 mm under a load of 80 kN and the load at elasti limit is 102 kN The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation. (iv) Percentage reduction in area. (v) Ultimate tensile stress
1. A specimen of steel 20 mm diameter with a gauge length of 200 n.m is tested io destruction. It' has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i) The stress at elastic limit. (ii) Young's modulus. (iii) Percentage elongation. (iv) Percentage reduction in area. (v) Ultimate tensile stress
A steel specimen is tested in tension. The specimen is 25 mm wide by 12.5 mm thick in the test region. By monitoring the load dial of the testing machine, it was found that the specimen yielded at a load of 160 kN and fractured at 214 kN. a. Determine the tensile stress at yield and at fracture. b. If the original gauge length was 100 mm, estimate the gauge length when the specimen is stressed to 1/2 the yield stress.